The Mingke MT1050 belt grade is made of low carbon, martensitic,stainless steel of type 15-7 PH or 14-7 PH and is characterised by:

  ● Excellent static strength

  ● Excellent fatigue strength 

  ● Good corrosion resistance 

  ● Very good wear resistance 

  ● Very good repairability


MT1050 is a high strength steel with excellent mechanical properties. This, in combination with good 

corrosion , makes it the ideal choice for applications in very harsh conditions. Another advantage is that 

it is easy to repair.


Chemical Composition (Nominal) %

C

Si

Mn 

Cr 

Ni 

Cu 

Ti 

Mo

0.08

1.5

1.0

14

7

0.7

0.3

0.8


Forms of Supply

The belts are, as standard, delivered in a heat-treated condition with a mill finish and have well-rounded 

edges. If required practically any surface finish can be supplied. Perforated belts are also available. The 

belts are levelled and straightened to obtain optimal flatness and straightness. The belts can be supplied 

in open lengths, with the ends prepared for welding on site, or in endless condition with a welded joint. For

tracking, the belts can be provided with V-ropes, either rubber or in the form of a specially designed steel 

spiral. If required, the product side of the belt can be fitted with retaining strips to keep the conveyed 

material on the belt or with transverse flights to pre- vent material from sliding backwards when the belt 

is steeply inclined. Different tolerance grades are available to ensure that the best belt can be selected 

from an economic point of view.


Mechanical Properties 

Static Strength 

Static strenght Standard strength at room temperature, nominal values

Position

Propor-tional Limit

Yield Strength

Tensile Strength

Elongation

(A5%)

Weld Factor

Rm/Rm

Hardness

HV5

 

 

Mpa

Ksi

Mpa

Ksi

 

 

 

Parent material

 

1100

161

1150

167

8

 

380

Transverse weld(not heat treated)

 

 

1080

 

157

 

1130

 

164

 

 

0.98


MT1050 should not be exposed for prolonged periods (a few hours) to temperatures exceeding 250°C

 (480°F) as a change (increase) in strength due to precipitation hardening takes place at high temperatures.

Hence the following recommendation: If an operation temperature of or above 250°C (480 °F) is considered, 

your local Mingke office should be contacted for technical assistance.


Impact Properties 

This belt grade is not recommended for use at low temperature e.g such as in freezing operations. 

Dynamic Strength The fatigue limit is defined as the reverse bending stress at which 50% of the test 

specimen withstand a minimum of 2x106 load cycles. These values refer to 20°C (68 °F), a normal 

dry atmosphere and standard prepared specimen. The fatigue limit for the parent material is 

approximately ± 500 MPa (73 Ksi).


Physical properties 

Modulus of elasticity, E

197000 Mpa

28600 Ksi

Density,

7740 Kg/m3

0.280 lb/in3


Thermal Conductivity, λ

Temp,   °C

20

100

200

300

400

°F

68

212

392

572

752

W/mK

15

16

18

19

20

Btu/ft h °F

8.7

9.2

10.4

11

11.6


Specific Heat, Cp 

Temp, °C

20

100

200

300

400

°F

68

212

392

572

752

kJ/kgK

 

0.5

90.5

 

 

Btu/lb °F

 

0.12

0.12

 

 


Thermal Expansion, α

Temp, °C

20-100

20-200

20-300

20-400

°F

68-212

68-392

68-572

68-752

10-6/ °C

10.9

11.5

11.7

11.9

10-6/ °F

6.1

6.4

6.5

6.6


Resistivity, ρ

At 20° C  (68° F)     0,8 µΩm


Magnetic Properties

Remanence, Br                                   0.01Wb/m2

Coercive force, Hc                              <1500A/m

Max relative permeability, µr               1

The thermal conductivity of precipitation hardened steel is compa- rable to austenitic stainless steels, but the 

thermal expansion is much lower. This makes the precipitation-hardened steel less sensi- tive to thermal 

strain and buckling caused by uneven temperature.


Corrosion Resistance 

General Corrosion 

MT1050 shows a good corrosion resistance in rural and mild industrial atmosphere and almost equal good when expose to coastal atmosphere.

It has good resistance to:

  ● Organic acids, such as acetic acid, up to high concentrations and high temperatures and formic acid at low concentrations and high temperatures.

  ● Inorganic acids, e.g. sulphuric acid at low concentration and phosphoric and nitric acids at moderate concentration and temperatures.

  ● Ammonium hydroxide up to boiling point and sodium hydroxide at moderate concentrations and temperatures.

Mingke MT1050 is not suitable to use in any concentration of hydrochloric acid, or in phosphoric and nitric acids of high concentration and high temperature, and sulphuric acid of moderate and high concentration at elevated temperatures.


Pitting and Crevice Corrosion 

The steel may be sensitive to pitting, even in solutions of a relative low chloride content. When continuous 

operation at room temperature, Mingke MT1050 has good resistance to pitting providing that the belt is 

kept clean.


Stress Corrosion Cracking 

Stress corrosion cracking, although occurring relatively infrequently, can be cause of failure in stainless steels. 

It occurs at temperature above about 70° C  (160° F), if the steel is subjected to tensile stresses and comes 

into contact with certain solutions, particularly those containing chlorides. 


Hydrogen Embrittlement 

Hydrogen embrittlement is a potential danger to all high strength martensitic steels whenever the reduction of 

hydrogen ions to atomic hydrogen occurs. If this is the case, contact your local Mingke office.


Weldability

Welding Joints with very good strength and toughness can be formed in MT1050. A suitable fusion 

welding method is gas-shielded arc welding, with the TIG method as first choice.


Scope of Supply

Width: 1000 / 1200 / 1550 / 2000 / 3000 / 4000 ...9000 mm

Thickness: 1.0 / 1.2 / 1.8 / 2.2 / 2.7 / 3.0 mm

Tips: Max. width of a single belt is 1550mm, customized sizes via cutting or longitudinal welding are available