High Strength Carbon Steel Belt

 

Mingke CT1100 (previous model: MK-1100C) is a carbon steel with a hard, smooth surface, which makes it suitable for any application with a low risk for corrosion. Very good thermal properties make it ideal for baking and for heating and drying of liquids, pastes and fine-grained products.

 

Chemical Composition (Nominal) %

C

Mn

P

S

Fe

0.6-0.7

0.6-0.9

0.04

0.05

98.31-98.8

 

Static Strength

Standard strength at room temperature, nominal values

Parameters

Yield strength

Tensile strength

Elongation

Weld factor

Hardness

 

Mpa

Ksi

Mpa

Ksi

A5(%)

Rm/Rm

HV5

Parent material

1050

152

1150

167

7

0.75

350

Welding area

800

116

900

130

*

*

*

 

Dynamic Strength

The fatigue limit is defined as the reverse bending stress at which 50% of the test specimen withstand a minimum of 2x106 load cycles. These values refer to 20°C (68°F), a normal dry atmosphere and standard prepared specimen. The fatigue limit for the parent material is approximately ± 460 Mpa (67 Ksi).

 

Weldability

Joints with very good strength and toughness can be formed in CT1100. A suitable fusion welding method is gas-shielded arc welding, with the TIG method as first choice.

A well-balanced heat-treatment must be performed in connection with the welding, to ensure the weld has good static and dynamic mechanical properties.

 

Scope of Supply

Length customize available

Width – 1200 / 1500 mm

Thickness – 1.2 mm

Tips: Max. width of a single belt is 1200mm, customized sizes via cutting or longitudinal welding are available.